High Temperature And Wear Resistance Phosphate High Alumina Bricks For Cement Rotary Kiln

Name: High Temperature And Wear Resistance Phosphate High Alumina Bricks For Cement Rotary Kiln
Brand: RONGSHENG
Price: 1 USD

China High Temperature And Wear Resistance Phosphate High Alumina Bricks For Cement Rotary Kiln wholesale

Brand Name : RONGSHENG

Certification : ISO9001

Place of Origin : Henan, China

Density : 2.2-2.4g/cm3

Material : High Alumina

Oem : YES

Surface : Smooth

Feature : Good Thermal Shock Resistance

Thermal Expansion : Low

Application : High Temperature Furnace Lining

Cold Crushing Stren : 45-80

Heat Capacity : High

Porosity : Low

Dimension : ISO size

Bending Strength : ≥25MPa

Bulk Density : ≥2.6g/cm³

Experience : 30 years

Corrosion Resistance : High

Contact Now

High temperature and wear resistance phosphate high alumina bricks for cement rotary kiln

High Temperature And Wear Resistance Phosphate High Alumina Bricks For Cement Rotary Kiln

Product Description

Phosphate bonded high alumina bricks are made from high alumina bauxite aggregate, selecting phosphoric acid or aluminum phosphate as binder. Finished phosphate bonded high alumina brick must go through 400~600 ℃ heating process and semi-dry compress process. Featured by high wear-resistance, high refractoriness and good thermal shock resistance, phosphate bonded high alumina bricks are widely used in rotary cement kiln transition zone, sintering zone, cooling zone and cooler working layer.

Phosphate Bonded High Alumina Bricks Features:

High mechanical strength
High refractoriness
Good wear resistance
Good spalling resistance

High Temperature And Wear Resistance Phosphate High Alumina Bricks For Cement Rotary Kiln

Specification

Phosphate Bonded High Alumina Brick Parameters

Item	Specification
	PA	PW	SP
Al2O3 %	≥75	≥77	≥80
Fe2O3 %	≤2.5	≤2.1	≤1.8
CCS, MPa	≥70	≥75	≥80
Bulk Density, g/cm3	≥2.70	≥2.65	≥2.90
0.2MPa RUL℃	≥1350	≥1300	≥1520
TSR, Cycle 1100℃ Water	≥20	≥20	≥20

Application

High Temperature And Wear Resistance Phosphate High Alumina Bricks For Cement Rotary Kiln

Phosphate Bonded High Alumina Bricks Application

1.Glass melting furnace, ceramic frit kiln, sodium silicate furnace, soaking furnace, ceramic kiln, etc
2.Coke oven’s coking chamber, combustion chamber walls, steel open-hearth ‘s regenerator and sediment chamber, etc.
3.Load-bearing parts of high temperature hot air furnace and acid open-hearth furnace roof, etc.

Product Tags:

High Temperature And Wear Resistance Phosphate High Alumina Bricks For Cement Rotary Kiln Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Zhengzhou Rongsheng Refractory Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!

High Temperature And Wear Resistance Phosphate High Alumina Bricks For Cement Rotary Kiln

High Temperature And Wear Resistance Phosphate High Alumina Bricks For Cement Rotary Kiln

High Temperature High Alumina Bricks

Cement Rotary Kiln High Alumina Bricks

Wear Resistance High Alumina Bricks

High Temperature And Wear Resistance Phosphate High Alumina Bricks For Cement Rotary Kiln Images